Flashforge resin is ideal for repid prototyping and product developing.
Estimated to ship 1-7 business days after payment confirmation.
FH1100
Whether suspended structure or smooth surface, FH1100′ modeling effect is very good, the surface of result is smooth and clean and high details in reduction. Designed for high precision pattern production, Flashforge FH1100 is ideal for repid prototyping and product developing.
With strict requirement of manufacturing, Flashforge FH1100 has high stability, with low shrinkage and low failure rate.
Material Properties
Density: 1.09-1.12g/ml
Viscosity: 400-550cps
Tensile Strength: 42 MPa
Elongation at Break: 17%
Shore Hardness: 85 D
Exposure Ec: 6 mj/cm2
Penetration Depth: 8 mil(0.2mm)
FH1200
·Accurate prong placement ·Smooth surface finish ·Captures fine detail
Flashforge’s castable resin has the merit of nontoxic, low odor, high detail, and rapid curing. The printed models show good strength, toughness, flexibility and high impact resistance. The resin burns out cleanly with no ash or residue.
Material Properties
Tensile Strength: 10 MPa
Elongation at Beak: 8.5%
Flexural Strength: 27 MPa
Flexural Modulus: 920 MPa
Shore Hardness: 70D
Volumetric Shrinkage: 5.58%-6.02%
Applications: Jewelry
FHD1200
Tensile strength: 35-42MPa
Elongation at break: 10~20%
Flexural strength: 62-70Mpa
Density: 1.038g/ml
Shore hardness: 84D
Volume contraction rate: 2.5%
Viscosity:50±20 mPa.s
FHD1300
Tensile strength: 60.5MPa
Elongation at break: 0.04
Density: 1.118g/ml
Shore hardness: 81D
Volume contraction rate: 6.74%
Viscosity: 120cps
FHD1400
Tensile strength: 45MPa
Elongation at break: 15%
Flexural strength: 53MPa
Flexural modulus: 1200MPa
Density: 1.09-1.12g/ml
Shore hardness: 82D
Volume contraction rate: 3-5%
Viscosity:350-500cps
Size: Big Package(37.5*15.5*23.5cm)/Small Package(14*7*21.5cm)
specification: 500ml*10/500ml*2